Corrosion fatigue crack growth in clad low-alloy steels Part 1, medium-sulfur forging steel.

Corrosion fatigue crack growth in clad low-alloy steels [electronic resource] : Part 1, medium-sulfur forging steel.

Corrosion fatigue crack propagation tests were conducted on a medium- sulfur ASTM A508-2 forging steel overlaid with weld-deposited Alloy EN82H cladding. The specimens featured semi-elliptical surface cracks penetrating approximately 6.3 mm of cladding into the underlying steel. The initial crack si...

Full description

Saved in:
Bibliographic Details
Online Access: Online Access
Corporate Author: Bettis Atomic Power Laboratory (Researcher)
Format: Government Document Electronic eBook
Language:English
Published: Washington, D.C. : Oak Ridge, Tenn. : United States. Dept. of Energy ; distributed by the Office of Scientific and Technical Information, U.S. Dept. of Energy, 1996.
Subjects:
Low Alloy Steels.
Crack Propagation.
Reactor Materials.
Cracks.
Reactor Components.
Steel-astm-a302.
Fatigue.
Testing.
Steel-astm-a508.
Nuclear Reactor Technology ;36 Materials Science.

Internet

Online Access

Online

Holdings details from Online
Call Number: E 1.99:CONF-9604120--2-Pt.1
E 1.99:CONF-9604120--2-Pt.1 Available

Similar Items